Glass Cord

CENTRAL GLASS RUBBER COATED YARN (Rubber Coated Glass Cord, Rubber Impregnated Glass Cord) is produced by gathering with the special binder and also treated by RFL, then twisted together.

Uses

This product could be widely used as material for reinforcing the synchronous belts (transmission belts) for automotive, office equipments and other machineries.

Products

Rubber Coated Glass Cord for Synchronous Belt
(Typical Construction and Physical Properties for reference) Central Glass Co.,Ltd

1. for Chloroprene (Neoprene) Rubber <Peel Method>

		Loss of ignition	TWIST	Diameter	Tensile Strength	Adhesive Strength	Weight per Bobbin	No. of Bobbin in one box
Construction	Tex g/cm2	%	TURN	mm	N	N/25mm	kg	No.

ECG150- 3/0 -4.0 S & Z -B-18	126	19		0.25	73.5<	196<	1.7	8
ECG150- 5/0 -3.0 S & Z -B-18	208	19		0.37	147<	196<	2	8
ECG150- 3/2 -3.6 S & Z -B-18	254	19		0.45	147<	196<	1.7	8
ECG150- 6/0 -4.0 S & Z -B-18	254	19		0.45	127<	196<	1.7	8
ECG150- 3/3 -3.6 S & Z -B-18	370	19		0.53	196<	196<	1.8	8
ECG150- 9/0 -3.5 S & Z -B-18	375	19		0.51	235<	196<	2	8
ECG150- 3/6 -2.0 S & Z -B-18	760	19		0.80	392<	196<	5	2
ECG150- 3/8 -2.5 S & Z -B-18	1,020	19		0.94	559<	196<	10	2
ECG150- 3/10-2.0 S & Z -B-18	1,270	19		1.00	637<	196<	10	2
ECG150- 3/11-2.0S & Z -B-18	1,390	18		1.05	705<	196<	9	2
ECG150- 3/13-2.0 S & Z -B-18	1,650	18		1.20	833<	196<	10	2
ECG150- 10/15-1.1 S & Z -B-18	6,240	16.7		2.20	2,716<	196<	10	2
ECG50- 1/0 -4.0S & Z -B-18	126 +/- 8	18.0 +/- 3.0	4.0 +/- 0.4	0.25 +/- 0.04	73.5<	196<	1.6 +/- 0.2	8
ECG50- 2/0 -4.0S & Z -B-18	254 +/- 16	18.0 +/- 3.0	4.0 +/- 0.4	0.45 +/- 0.08	152<	196<	1.9 +/- 0.2	8
ECG50- 1/2 -3.6S & Z -B-18	254 +/- 16	18.0 +/- 3.0	3.6 +/- 0.3	0.45 +/- 0.08	152<	196<	3.2 +/- 0.4	8
ECG50- 1/3 -3.6S & Z -B-18	370 +/- 25	18.0 +/- 3.0	3.6 +/- 0.3	0.53 +/- 0.08	196<	196<	2.4 +/- 0.3	8
ECG50- 1/11-2.0S & Z -B-18	1,390 +/- 90	18.0 +/- 3.0	2.0 +/- 0.2	1.05 +/- 0.10	705<	196<	9.0 +/- 1.0	2
ECG50- 1/13-2.0S & Z -B-18	1,650 +/- 100	18.0 +/- 3.0	2.0 +/- 0.2	1.20 +/- 0.10	833<	196<	10.0 +/- 1.0	2
ECG50- 1/0 -4.0S & Z -B-18B	122 +/- 8	16.5 +/- 3.0	4.0 +/- 0.4	0.25 +/- 0.04	73.5<	196<	1.5 +/- 0.2	8
ECG50- 2/0 -4.0S & Z -B-18B	246 +/- 16	16.5 +/- 3.0	4.0 +/- 0.4	0.40 +/- 0.08	152<	196<	1.8 +/- 0.2	8
ECG50- 1/2 -3.6S & Z -B-18B	246 +/- 16	16.5 +/- 3.0	3.6 +/- 0.3	0.40 +/- 0.08	152<	196<	3.1 +/- 0.4	8
ECG50- 1/3 -3.6S & Z -B-18B	360 +/- 25	16.5 +/- 3.0	3.6 +/- 0.3	0.53 +/- 0.08	196<	196<	2.3 +/- 0.3	8
ECG50- 1/6 -2.0S & Z -B-18B	730 +/- 50	16.5 +/- 3.0	2.0 +/- 0.2	0.74 +/- 0.08	392<	196<	9.0 +/- 1.0	2
ECG50- 1/10-2.0S & Z -B-18B	1,240 +/- 80	16.5 +/- 3.0	2.0 +/- 0.2	1.00 +/- 0.10	637<	196<	8.0 +/- 1.0	2
ECG50- 1/11-2.0S & Z -B-18B	1,390 +/- 90	16.5 +/- 3.0	2.0 +/- 0.2	1.05 +/- 0.10	705<	196<	9.0 +/- 1.0	2
ECG50- 1/13-2.0S & Z -B-18B	1,600 +/- 100	16.5 +/- 3.0	2.0 +/- 0.2	1.20 +/- 0.10	833<	196<	10.0 +/- 1.0	2
ECG50- 3/9 -2.0S & Z -B-18B	3,280 +/- 180	16.5 +/- 3.0	2.0 +/- 0.2	1.70 +/- 0.10	1,500<	196<	10.0 +/- 1.0	2
ECG50- 3/16-1.1S & Z -B-18B	6,000 +/- 300	16.5 +/- 3.0	1.1 +/- 0.1	2.20 +/- 0.10	2,300<	196<	10.0 +/- 1.0	2
ECG50- 3/23-1.1S & Z -B-18B	8,425 +/- 300	16.5 +/- 3.0	1.1 +/- 0.1	2.75 +/- 0.15	2,600<	196<	10.0 +/- 1.0	2

2. for H-Nitrile Butadiene Rubber (H-NBR)

Construction	Tex	Loss of ignition	TWIST	Diameter	Tensile Strength	Adhesive Strength	Weight per Bobbin	No.of Bobbin in one Box

ECG150- 3/13-2.0 S & Z-A-26-OC	1,747	22.5	2.0	1.17	882<	177<	11	2
ECG150- 3/11-2.0 S & Z-A-51-OC	1,390 +/- 100	22.5 +/- 3.0	2 +/- 0.2	1.08 +/- 0.1	830<	195<	11	2

3. for Urethane Rubber

Construction	Tex	Loss of ignition	TWIST	Diameter	Tensile Strength	Weight per Bobbin	No.of Bobbin in one Box

ECG150- 3/0 -3.7 S & Z-PU-08	126	16	3.7	0.30	65<	1.8	8
ECG150- 2/0 -3.7 S & Z-PU-08	84	16	3.7	0.24	49<	1.2	8

4. Further information

(1)It is available to supply further kinds of FRR cord.
(2)Diameter of glass fiber filament is about 9 micron meter.
(3)Base components of FRR cord are 200 or 600 filaments ( both 9
micron Yarn ) strand and these are treated with Resorcinol-
Formaldehyde-Latex(RFL).